STAINLESS STEELS


AWS A5.9: ER316L

MIG/TIG Filler wire for the joining and overlay of Stainless Steels of similar composition. Joining of all Austenitic Stainless. Used in the food and Dairy IndustryAustenitic deposit with up to 12% Ferrite, slightly magnetic.

AWS A5.9: ER316LSi

Solid MIG/TIG Filler wire for the joining and overlay of Stainless Steels of similar composition, (Moly-bearing) such as found in the Food/Drink Industry. Essentially Austenitic, with up to 13% Ferrite, making the deposit slightly magnetic. Increased silicon content for more fluid deposit over 316L

AWS A5.9: ER308L

MIG/TIG Filler wire for the joining and overlay of Stainless Steels of similar composition such as AISI 304L. Low carbon content minimises Carbide precipitation.

AWS A5.9: ER308LSi

MIG/TIG Filler wire for the joining and overlay of Stainless Steels of similar composition such as AISI 304L Low carbon content minimises Carbide precipitation. Higher silicon content than 308L gives increased fluidity.

AWS A5.9: ER307

Stainless Steel MIG/TIG Filler wire with a significant amount of Manganese, making the deposit fully Austenitic. Joining of Austenitic Stainless to Carbon Steels as well as 14% Manganese. Used to join Wear Plates and as a Buffer layer under hard surfacing. Fully Austenitic deposit, non-magnetic with high ductility.

AWS A5.9: ER307~

MIG Filler wire for the joining and overlay of Stainless Steels of similar composition. Joining of all Austenitic Stainless as well as 14% Manganese. Used to join Wear Plates and as a buffer layer under hard surfacing. Fully Austenetic deposit, non-magnetic with high ductility. Increased Silicon content compared with standard, gives more fluid deposit.

AWS A5.9: ER430

Ferritic Stainless Steel Filler wire for the joining and overlay of Stainless Steels of similar composition. Used for the welding of Exhaust components, casting reclamation and fabrication of pipework used in automotive, paper and chemical process plant.

AWS A5.9: ER385

MIG/TIG Filler wire for the joining and overlay of Stainless Steels of similar composition (904L). Due to its alloy composition, high Mo-content and Cu, the weld metal is suited against attacks by phosphoric and sulphuric acids, it shows a high resistance against pitting and stress corrosion in chloride containing media.

AWS A5.9: ER309

MIG/TIG Filler wire for the joining and overlay of Stainless Steels of similar composition, such as AISI 309 castings. High carbon content for maximum strength and corrosion resistance

AWS A5.9: ER309Lsi

MIG/TIG Filler wire for the joining and overlay of Stainless Steels of similar composition, such as AISI 309 castings. Low carbon content minimises Carbide precipitation. May also be used as a dissimilar consumable and for joining 3Cr12.Increased Silicon content over 309L for fluiditity.

AWS A5.9: ER309L

MIG/TIG Filler wire for the joining and overlay of Stainless Steels of similar composition, such as AISI 309 castings. Low carbon content minimises Carbide precipitation. May also be used as a dissimilar consumable and for joining 3Cr12.

AWS A5.9: ER310

MIG/TIG Filler wire for the joining and overlay of Stainless Steels of similar composition, such as AISI 310 castings. Fully Austenitic deposit makes it Non Magnetic. Resistant to scaling at temperatures up to 1050°C.

AWS A5.9: ER312

Stainless Steel Filler Wire with a Duplex structure for the joining of dissimilar steels, low alloy steels to Stainless. Also used to provide a buffer layer prior to hard facing. Work Hardens to some degree. High resistance to impact. Can also be used for joining Wear Plates to mild steel support structures.

AWS A5.9: ER316H

High Carbon MIG/TIG Filler wire for the joining and overlay of Stainless Steels of similar composition, i.e. 316H. Joining of most Austenitic Stainless. Used in the food and Dairy Industry and where higher strength than 316L is required.Austenitic deposit with up to 10% Ferrite, slightly magnetic.

AWS A5.9: ER317L

MIG/TIG Filler wire for the joining and overlay of Stainless Steels of similar composition. Joining of all Austenitic Stainless. Used in the food and Dairy IndustryAustenitic deposit with up to 12% Ferrite, slightly magnetic.

AWS A5.9: ER347

Solid MIG/TIG Filler wire for the joining and overlay of Stabilized Stainless Steels of similar composition, Essentially Austenitic, with up to 12% Ferrite, making the deposit slightly magnetic. Stabilised with Niobium to overcome Titanium transfer problems in 321. Operating temperature range -196°C – 815°C.

AWS A5.9: ER420

TIG Filler wire for the joining and overlay of Stainless Steels of similar composition (Straight Chrome) Martensitic deposit, which is hardenable. Higher carbon version of 410.

 

AWS A5.9: ER410

TIG Filler wire for the joining and overlay of Stainless Steels of similar composition (Straight Chrome) Martensitic deposit, which is heat treatable. Can be used to repair Plastic mould steels of similar composition.

AWS A5.9: ER2209

MIG/TIG Filler wire for the joining and overlay of Stainless Steels of similar composition (Duplex). The analysis of the wire is overmatched with respect to the base material to ensure the correct microstructure when welded. Used in the fabrication of plate and pipework in the petro-chemical and offshoe industry.

AWS A5.9: ER2594

MIG/TIG Filler wire for the joining and overlay of Stainless Steels of similar composition (Super Duplex). The analysis of the wire closely matches the base material to ensure the correct microstructure when welded. Used in the fabrication of plate and pipework in the Petro-chemical and Offshoe industries. PREN >40.